SEMI-STRUCTURAL
ACRYLIC BONDING FOAM |
| |
HYPER
JOINT
H9004, H9008, H9012
 |
| |
| Nitto Hyper Joint 9004 – 9008
and 9012 ranges offer higher bonding force, high
resistance to mechanical, static and dynamic stresses,
outdoor and in the worst environmental conditions.
|
| |
Strengths
- Resistance to high temperatures and to water
also when immersed.
- High conformability and different substrates
(powder paints included)
- Opportunity to be cut and ready to apply
|
|
 |
Code |
Thickness |
Width |
Length |
H9004 |
0.4* |
3
˜ 450
mm |
20
mt |
H9008 |
0.8* |
H9012 |
1.2* |
|
| |
* Thickness without liner |
Resistance
to physical/mechanical stresses |
Hyper-conformability
|
| |
|
Evaluation
category |
H9004 |
H9008 |
H9012 |
Initial value
(23°Cx30 minutes) |
97 |
52 |
40 |
Normal condition
(23°Cx24 hours) |
110 |
74 |
55 |
Heat resistance
(80°Cx250 hours) |
160 |
150 |
136 |
Water resistance
(40°C water temperature x 250 hours) |
160 |
75 |
69 |
| Thermal cycle resistance*
|
95 |
76 |
62 |
*Cycle conditions:
(80°C x 16 hours - 23°C x 1 hour - 50°C
x 98% RHx24 hours - 23°Cx1hour - -30°Cx8hours
- 23°Cx1hour) was carried out for 10 cycles
|
|
H9008
Competitor's
0.8mmt |
H9012
Competitor's
1.2mmt |
Testing method:
place 25mm-wide acrylic foam on an uneven acrylic
palate, pressure only one way with 5Kg roler. Then
measure Wet-out ratio from inderside. (Distance:
100µm, Interval: 20mm) |
APPLICATIONS |
| |
AERO-NAVAL
SECTOR |
| |
|
|
| |
|
|
|
| |
|
HIGH
TECH |
| |
|
|
| |
|
BUILDING
AND CONSTRUCTION |
| |
|
|
| |
|
|
|
| |
|
|
| |
AUTOMOTIVE |
| |
|
|
|
|
Stainless steel 
Alluminium plate 
Acrylic plate 
ABS plate 
Polycarbonate plate 
Polyethylene plate 